Herein the photoluminescence spectra of nanosized cubic Y2O3:Tb3+ having Tb3+ concentrations varying between 0.1 and 10 Mol% are described. Low temperature cathodoluminescence spectra from these materials recorded in a scanning transmission electron microscope are presented and discussed. By studying the photoluminescence-spectra recorded at room temperature and focused on the 5D4→7F5 (C2) and 5D4→7F5 (C3i) transitions, at 542.8 and 544.4 nm respectively, it was found that the critical distance for energy transfer from Tb3+ ions at C3i lattice sites to Tb3+ ions at C2 lattice sites was 1.7 nm; at distances >1.7 nm, which prevail at low Tb3+ concentration, this energy transfer virtually stops. The gradual change of the excitation spectra upon increasing the Tb3+ concentration is also explained in terms of energy transfer from Tb3+ at C3i sites to Tb3+ at C2 sites. Cathodoluminescence spectra recorded at low temperatures with the scanning transmission electron microscope provided additional evidence for this radiationless energy transfer.
Symmetry-related transitions in the photoluminescence and cathodoluminescence spectra of nanosized cubic Y2O3:Tb3+
Resource category